Abstract
According to previous studies on the fracture surface morphologies of bulk metallic glasses, the stable crack growth region width and vein pattern size increase with the plasticity at room temperature. In the present work, the fracture surface morphologies of Ti- and Zr-based bulk metallic glasses bent over a wide temperature range (0.1–0.8 glass transition temperature) are systematically analyzed. According to our finding, the stable crack growth region width increases while the vein pattern size decreases as the ductility improves by varying temperature. This observation is in contrast to the common thought that the ductility is proportional to the stable crack growth region width and vein pattern size simultaneously. Moreover, the vein pattern size and shear offset width are found to be almost equal at a specific temperature. Furthermore, smaller vein pattern size and shear offset width reduce shear band instability and, consequently, enhance the ductility.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.