Abstract
The purpose of this research was to determine the behavior of modified sulfonated poly (ether ether ketone) (SPEEK) with degree of sulfonation (DS) 68% blended by charged surface modifying macromolecule (cSMM) at different operating temperatures (room to 80°C) for direct methanol fuel cell application. The fabricated SPEEK (68)/cSMM membrane was compared with SPEEK (68) and Nafion112 membranes in terms of water uptake, proton conductivity, and methanol permeability at relatively high temperatures. The water uptake of SPEEK (68)/ cSMM was higher than that of SPEEK (68) and Nafion112 over the temperature ranges studied; however it was dissolved at 80°C. Proton conductivity of SPEEK (68)/cSMM showed improvement compared to SPEEK (68) at temperature range, but still lower than Nafion112, moreover methanol permeability behavior of fabricated membrane was lower at high temperatures as compared to that of SPEEK and Nafion112 and better overall performance was allocated to the fabricated membrane at 60°C.These results indicate that SPEEK (68)/cSMM membrane is promising to be used as a proton exchange membrane in direct methanol fuel cell.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Applied Membrane Science & Technology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.