Abstract
The FeCrSiNiCoC coatings with fine macroscopic morphology and uniform microstructure were made on 1Cr11Ni heat resistant steel substrate by a laser-based cladding technique. The coating consists of dendritic γ-Fe and eutectic Fe-Cr intermetallic with an average microhardness of 467 HV0.5 ± 22.6 HV0.5. At the load of 200 N, the average friction coefficient of the coating dropped as temperature increased, while the wear rate decreased and then increased. The wear mechanism of the coating changed from abrasive wear, adhesive wear and oxidative wear to oxidative wear and three-body wear. Apart from an elevation in wear rate with increasing load, the mean friction coefficient of the coating hardly changed at 500 °C. Due to the coating's transition from adhesive wear and oxidative wear to three-body wear and abrasive wear, the underlying wear mechanism also shifted.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.