Abstract
SnS nanocrystals were synthesized using bis(phenylpiperazine dithiocarbamate)tin(II) in oleic acid (OA) and octadecylamine (ODA) at three different temperatures (150, 190, and 230°C). XRD diffraction pattern confirms that OASnS and ODASnS nanoparticles are in the orthorhombic phase and the type of capping agent used affects the crystallinity. Transmission electron microscopy (TEM) images shows spherically shaped nanocrystals for oleic acid capped SnS (OASnS) while octadecylamine (ODASnS) are cubic. Monodispersed SnS of size range 10.67–17.74 nm was obtained at 150°C for OASnS while the biggest-sized nanocrystals were obtained at 230°C for ODASnS. Temperature and capping agents tuned the crystallite sizes and shapes of the as-prepared nanocrystals. Electron dispersive X-ray spectroscopy indicates the formation of tin sulphide with the presence of Sn and S peaks in the nanocrystals. Flowery and agglomerated spherical-like morphology were observed for ODASnS and OASnS nanocrystals, respectively, using a SEM (scanning electron microscope). Direct electronic band gaps of the synthesized SnS nanocrystals are 1.71–1.95 eV and 1.93–2.81 eV for OASnS and ODASnS nanocrystals, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.