Abstract

The first principle method based on density functional theory and generalized gradient approximation is used to investigate the interaction of Ta and Re elements at Ni/Ni<sub>3</sub>Al interface and their influence on the interface strength. According to the calculations of the dissolution energy of these two alloying elements at 7 different positions, it can be concluded that in most of the stoichiometric ranges, Ta atoms preferentially occupy Ni sites in the <i>γ</i> phase, while Re atoms occupy preferentially Al sites in <i>γ'</i> phase. The doping positions do not change when these two atoms are co-alloyed. The calculation of Griffith fracture work of Ni/Ni<sub>3</sub>Al interface system shows that the doping of Ta atoms can improve the interface fracture strength of the phase boundary region between the <i>γ</i>/<i>γ'</i> coherent atomic layer and <i>γ</i> atomic layer. The interface is easier to fracture in the phase boundary area between <i>γ</i>/<i>γ'</i> coherent atomic layer and <i>γ'</i> atomic layer after Ta atoms have been doped. The doping of Re atoms can improve the interface fracture strength of the phase boundary region between <i>γ</i>/<i>γ'</i> coherent atomic layer and <i>γ'</i> atomic layer. The interface is easier to break in the phase boundary area between <i>γ</i>/<i>γ'</i> coherent atomic layer and <i>γ</i> atomic layer. The calculation results of the unstable stacking fault energy under the interface slip system <inline-formula><tex-math id="M1">\begin{document}$ [110](001) $\end{document}</tex-math><alternatives><graphic xmlns:xlink="http://www.w3.org/1999/xlink" xlink:href="6-20222103_M1.jpg"/><graphic xmlns:xlink="http://www.w3.org/1999/xlink" xlink:href="6-20222103_M1.png"/></alternatives></inline-formula> before and after Ta and Re alloying show that the doping of these two types of atoms increases the value of the unstable stacking fault energy of the interface, and the slip system<inline-formula><tex-math id="M2">\begin{document}$ [110](001)$\end{document}</tex-math><alternatives><graphic xmlns:xlink="http://www.w3.org/1999/xlink" xlink:href="6-20222103_M2.jpg"/><graphic xmlns:xlink="http://www.w3.org/1999/xlink" xlink:href="6-20222103_M2.png"/></alternatives></inline-formula> becomes difficult to start, which enhances the ability of the interface to block the movement of dislocations, thus enhancing the creep strength of the nickel base superalloy. When doping Re atoms, the effect is greater, and the unstable stacking fault energy of the interface increases by 11.1%, which is better for improving the creep strength of the system. By studying the influence of alloying atoms on the path of vacancy migration and the energy barrier, it is concluded that the doping of Ta and Re atoms can increase the vacancy formation energy and the potential barrier of vacancy migration at the interface. The doping of Re atoms increases the migration energy barriers on both sides of the interface, and the doping of Ta atoms increases the migration energy barriers of <i>γ</i> phase. The increase of the migration barrier hinders the emission and absorption of vacancies, thereby improving the creep capability of the alloy.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.