Effect of synthesis route on the multiferroic properties of BiFeO3: A comparative study between solid state and sol–gel methods

Abstract

Polycrystalline BiFeO3 (BFO) powder was prepared through optimized solid state (SS) and sol–gel (SG) reaction methods. The effect of preparation routes on the crystal purity and multiferroic properties of the BFO was investigated. Sol–gel synthesis results almost a single-phase material at relatively lower temperatures while the solid-state method results into BFO with a small amount of Bi2Fe4O9 secondary phase. The grain size of SG processed sample reduces to half the size of the one that is prepared by SS. Elemental analysis shows a stoichiometric Bi:Fe content for SG samples by restricting the Bi loss. In comparison with the SS samples, dielectric constant of SG samples exhibit higher values with Maxwell–Wagner type dielectric dispersion. A cusp at 50 K was seen in M–T curves for SS samples, for which no frequency dependence was observed in a.c susceptibility measurements ruling out the earlier predictions of spin glass nature in this system. M−H loops show a typical antiferromagnetic nature at 300 K while a weak ferromagnetic behavior is found at 10 K. A slight increase in HC and Mr was observed for SG samples over SS. The improved properties of SG processed BFO makes it more promising for applications.