Abstract
Yttrium iron garnet (YIG) (Y 3Fe 5O 12) powders have been synthesized through a co-precipitation method in the presence of sodium bis(2-ethylhexylsulfosuccinate), AOT as an anionic surfactant. The garnet precursors produced were obtained from aqueous iron and yttrium nitrates mixtures using 5 M sodium hydroxide at pH 10. A statistical Box–Behnken experimental design was used to investigate the effect of the main parameters (i.e. AOT surfactant concentration, annealing time and temperature) on YIG powder formation, crystallite size, morphology and magnetic properties. YIG particles were investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), and vibrating sample magnetometer. XRD revealed that the formation of single cubic phase of YIG was temperature dependent and increased by increasing the annealing temperature from 800 to 1200 °C. SEM micrographs showed that the addition of AOT surfactant promoted the microstructure of YIG in crystalline cubic-like structure. The magnetic properties were sensitive to the synthesis variables of annealing temperature, time and AOT surfactant concentration. The maximum saturation magnetization (28.13 emu/g), remanence magnetization (21.57 emu/g) and coercive force (703 Oe) were achieved at an annealing temperature of 1200 °C, time 2 h and 500 ppm of AOT surfactant concentration.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.