Abstract
The fabrication of SrFe12O19 ferrite powders with good magnetic properties is a key process in the industrial production of permanent magnets. Remanence and coercivity of the powders was seriously decreased due to the generation of surface lattice defects produced during the crushing of pre-sintered ferrite powders. And the traditionally applied high-temperature annealing above 800 °C can only partially restore the magnetic properties. In this work, the effects of types, adding mode and contents of surfactant (hexadecyl trimethyl ammonium bromide, triethanolamine) on the magnetic properties of crushed powders of the pre-sintered SrFe12O19 ferrite under a low-temperature annealing of 400 °C process were systematically explored. The results showed that surfactants are beneficial to restore or even enhance the magnetic properties of the crushed powders compared with the pre-sintered ferrite due to the refinement of the particles and repairing the surface defects. The surfactant-assisted low-temperature annealing process proposed in this work will promote the commercial production of high performance ferrite powders and ferrite magnets, which can also effectively reduce the production energy consumption.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.