Abstract
The effect of surface grinding on the stress corrosion cracking (SCC) behavior of 304L austenitic stainless steel in boiling magnesium chloride has been investigated. SCC tests were conducted both without external loading and with varied levels of four-point bend loading for as-delivered material and for specimens which had been ground parallel or perpendicular to the loading direction. Residual stresses due to the grinding operation were measured using the X-ray diffraction technique. In addition, surface stress measurements under applied load were performed before exposure to evaluate the deviation between actual applied loading and calculated values according to ASTM G39. Micro-cracks initiated by a high level of tensile residual stress in the surface layer were observed for all the ground specimens but not those in the as-delivered condition. Grinding along the loading direction increased the susceptibility to chloride induced SCC; while grinding perpendicular to the loading direction improved SCC resistance. Surface tensile residual stresses were largely relieved after the initiation of cracks.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.