Abstract
Polymer-metal hybrid (PMH) joints of glass-fiber reinforced polypropylene random copolymer (GFRPPR) and aluminum alloy were prepared by the self-made hot pressing technology (HPT). The PPR copolymer was grafted with maleic anhydride and reinforced with 30% short glass fiber, and the aluminum alloy surface was anodized in oxalic acid and phosphoric acid solution, respectively. The PMH interfaces were mainly characterized by scanning electron microscopy (SEM), atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS) and contact angle tests. Anodized in the phosphoric acid solution, the anodized aluminum alloy surface showed needle-shaped honeycomb-like microstructures. The phosphoric acid anodized aluminum alloy surface was beneficial for polymer melt to flow into and form interlocking microstructures due to its micro porous structure, and the corresponding tensile shear strength and work of fracture reached up to 10.88 MPa and 16.15 kJ m−2, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.