Abstract
PurposeTo evaluate the effect of two surface modifications on early osseointegration parameters of conical implants in a translational pre-clinical model. Materials and methodsConical implants with progressive trapezoidal threads and healing chambers were evaluated consisting of two different surface conditions: 1) Implacil surface (IMP Sur), and 2) Implacil surface + Supplemental Acid-etching (IMP Sur + AE). Surface characterization comprised of the evaluation of roughness parameters (Sa, Sq and Sdr), surface energy and contact angle. Subsequently, implants were installed in the ilium crest of nine female sheep (weighing ~65 kg). Torque out, histological and histomorphometric analyses were conducted after 3 and 6 weeks in-vivo. The percentage of bone to implant contact (%BIC) and bone area fraction occupancy within implant threads (%BAFO) were quantified, and the results were analyzed using a general linear mixed model analysis as function of surface treatment and time in-vivo. ResultsSupplemental acid etching significantly increased Sa and Sq roughness parameters without compromising the surface energy or contact angle, and no significant differences with respect to Sdr. Torque-out testing yielded significantly higher values for IMP Sur + AE in comparison to the IMP Sur at 3- (62.78 ± 15 and 33.49 ± 15 N.cm, respectively) and 6-weeks (60.74 ± 15 and 39.80 ± 15 N.cm, respectively). Histological analyses depicted similar osseointegration features for both surfaces, where an intramembranous-type healing pattern was observed. At histomorphometric analyses, IMP Sur + AE implants yielded higher values of BIC in comparison to IMP Sur at 3- (40.48 ± 38 and 27.98 ± 38%, respectively) and 6-weeks (45.86 ± 38 and 34.46 ± 38%, respectively). Both groups exhibited a significant increase in %BAFO from 3 (~35%) to 6 weeks (~44%), with no significant differences between surface treatments. ConclusionSupplemental acid-etching and its interplay with implant thread design, positively influenced the BIC and torque-out resistance at early stages of osseointegration.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of the Mechanical Behavior of Biomedical Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.