Abstract
The thermal-mechanical fatigue (TMF) behaviour of CoCr22Ni22W14 was investigated under total strain controlled out-of-phase (OP) experiments without and with superimposed high cycle fatigue (HCF) loadings. The minimum temperature T min was 200 °C and the maximum temperature T max was varied between 750 and 1200 °C. The mechanical strain amplitude ε a,t me during pure TMF tests was kept equal to the thermal strain amplitude ε t th and the superimposed HCF amplitude ε a,t HCF was varied between 0.05 and 0.2%. In both loading conditions cyclic hardening is observed, which is the less pronounced the higher T max is. Only at T max=1200 °C, cyclic softening appears after cyclic hardening in the first cycles as a result of creep damage accumulation. With increasing superimposed HCF amplitudes, the cyclic deformation behaviour is obviously more and more determined by the superimposed HCF loadings. Due to the dynamic relaxation processes at higher temperatures, tensile mean stresses develop during all TMF tests performed. Under TMF-OP conditions a significant lifetime reduction is observed as a result of superimposed HCF loadings. This lifetime reduction increases with growing HCF amplitudes and may approach 90% of the fatigue lifetime obtained from pure OP experiments. For each T max the dependence between the total strain amplitude ( ε a,t= ε a,t me+ ε a,t HCF) and the number of cycles to failure can be described as a potential function ( ε a,t= A× N B −b) with an exponent b which decreases with increasing T max and which depends on the material properties at different temperatures.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.