Effect of superficially applied ZrO 2 inhibitor on the high temperature corrosion performance of some Fe-, Co- and Ni-base superalloys

Abstract

High temperature corrosion is an acute form of corrosion occurring at elevated temperature in the presence of an oxidizing gas and is associated with a thin electrolytic deposit (salt or ash) on alloy. Inhibitors and fuel additives have been used with varying success to combat oil ash corrosion. In this paper, the effect of an oxide additive namely ZrO 2 on the hot corrosion behaviour of some superalloys, viz. Superfer 800H (alloy A), Superco 605 (alloy B) and Superni 75 (alloy C) has been investigated in an Na 2SO 4–60%V 2O 5 environment at 900 °C for 50 cycles. Each cycle consisted of 1 h heating in a Silicon Carbide Tube furnace followed by 20 min cooling in ambient air. Weight change measurements after each cycle were taken by an electronic balance having an accuracy of 0.01 mg. XRD, SEM and EPMA analyses of the exposed specimens were carried out to characterize the oxide scales. In the Na 2SO 4–60%V 2O 5 environment, the corrosion rate for the Co-base alloy was found to be highest, whereas that for the Ni-base Superni 75 a lowest. Whereas, with ZrO 2 superficial coating, the overall weight gains got reduced for the alloys B and C, however the inhibitor was marginally effective in the alloy A. A thick scale was observed in the latter case, which was rich in Cr, Ni, Fe and V. Absence of protective continuous chromia layer and presence of less protective NiO was probably the main reason for more corrosion rate in this case.