Abstract

Abstract A magnesium coating with a low porosity and high microhardness was elaborated using cold spraying. However at present, a poor bonding strength between the coating and substrate limits its application. This paper aims at improving the bonding strength between the coating and substrate using substrate preheating. Aluminum substrates were heated to 100, 200 and 300°C respectively by a flame prior to cold spraying. The results show that substrate preheating can significantly increase the bonding strength. The bonding strength increased from 3.3±0.8 MPa to 11.6±0.5 MPa when the substrate temperature increased from room-temperature to 200°C. The fracture analyses show that the coating fracture occurred within the coating when the substrate was preheated at 200°C.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.