Effect of substrate and post-deposition annealing on nanostructure and optical properties of CdTe thin films

Abstract

Thermal evaporation is one of the promising methods for depositing CdTe thin films, which can obtain the thin films with the small thickness. In this work, CdTe nanoparticles have deposited on SiO2 substrates such as quartz (crystal) and glass (amorphous) at a temperature (Ts) of 150 °C under a vacuum pressure of 2 × 10−5 mbar. The thickness of CdTe thin films prepared under vacuum pressure is 100 nm. X-ray diffraction analysis (XRD) results showed the formation of CdTe cubic phase with a strong preferential orientation of (111) crystalline plane on both substrates. The grain size (D) in this orientation obtained about 7.41 and 5.48 nm for quartz and glass respectively. Ultraviolet-visible spectroscopy (UV–vis) measurements indicated the optical band gap about 1.5 and 1.52 eV for CdTe thin films deposited on quartz and glass respectively. Furthermore, to show the effect of annealing temperature on structure and optical properties of CdTe thin films on quartz and glass substrates, the thin films have been annealed at temperatures 50 and 70 °C for one hour. The results of this work indicate that the structure’s parameters and optical properties of CdTe thin films change due to increase in annealing temperature.