Abstract
Al 2O 3–TiC composites with a content of 30 wt% TiC with various size of starting powders were manufactured by hot pressing. The Vickers hardness, bending strength and fracture toughness were studied. The experiment results show that the starting powder size has a significant effect on the properties of the Al 2O 3–TiC composites. The maximum bending strength of the submicron Al 2O 3 with the fine TiC powders addition is 712 MPa, while the maximum fracture toughness of the same Al 2O 3 matrix with the large TiC powders addition is 6.5 MPa m 1/2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Refractory Metals and Hard Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.