Abstract
In this study, two similar, commercial polycrystalline Ni-based disk superalloys (LSHR and ME3) were creep tested at 760 °C and 552 MPa to approximately 0.3% plastic strain. LSHR consistently displayed superior creep properties at this stress/temperature regime even though the microstructural characteristics between the two alloys were comparable. High resolution structural and chemical analysis, however, revealed significant differences between the two alloys among active γ′ shearing modes involving superlattice intrinsic and extrinsic stacking faults. In ME3, Co and Cr segregation and Ni and Al depletion were observed along the intrinsic faults - revealing a γ′ to γ phase transformation. Conversely in LSHR, an alloy with a higher W content, Co and W segregation was observed along the intrinsic faults. This observation combined with scanning transmission electron microscopy (STEM) simulations confirm a γ′-to-D019 χ phase transformation along the intrinsic faults in LSHR. Using experimental observations and density functional theory calculations, a novel local phase transformation strengthening mechanism is proposed that could be further utilized to improve the high temperature creep capabilities of Ni-base disk alloys.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.