Abstract

In this study, electroless nickel (EN) plating was performed with stabilizer concentration to improve cavitation erosion resistance of gray cast iron under marine environment. Cavitation erosion tests were carried out in natural seawater solution in accordance with modified ASTM G32. The change of stabilizer concentration affected the plating rate, P content, and average crystal size of EN coating. The decrease of the plating rate with the stabilizer concentration and the flake-shaped graphite exposed to the gray cast iron surface negatively affected the cavitation erosion and corrosion prevention. In particular, cavitation erosion damage of EN coating was accelerated due to combined galvanic corrosion when the EN coating was destroyed and the substrate was exposed under the cavitation erosion environment.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.