Abstract
AbstractA useful instrument for polymer film preparation by solution casting was employed in this study. It enabled us to control the solvent evaporation rate of the polymer solution. By using this instrument, the aggregation of hard segments in segmented poly(urethane‐urea) (SPUU) was investigated. SPUU was prepared from poly(tetramethy1ene oxide), 4,4′‐diphenylmethane diisocyanate and ethylenediamine. The effect of solvent evaporation rate on the microphase‐separated structure of SPUU was elucidated by dynamic mechanical analysis, tensile test, differential scanning calorimetry analysis, small‐angle X‐ray scattering measurement, IR and IR dichroism analyses. The aggregation of hard segments in SPUU was observed to be affected considerably by the solvent evaporation rate of the cast film during the preparation. It was found that the slower the solvent evaporation rate, the higher the aggregation of hard segments to form rigid hard segment domains in SPUU. Nine months after casting, this casting effect still remained on the aggregation state of hard segments of SPUU films, although the interdomain spacing was not influenced by its rate.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.