Abstract
In the present work, Mn-N duplex stainless steels (DSS) were deposited on a SUS304 steel plate by plasma arc surfacing welding. The effect of solution treatment and the ratio of ferrite to austenite on the cavitation erosion (CE) behavior of Mn-N DSS coating were investigated. The results showed that depositing Mn-N DSS on other material surfaces through the weld overlay can solve the CE problems. It was found that the CE resistance of the sample treated at 1080 °C was higher than that of samples treated at higher temperatures. The excellent resistance to CE was related to the low ratio of ferrite to austenite that was adjusted by the solution treatment. During the CE process of Mn-N DSS coating, the mechanical factor was the dominating factor.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.