Abstract
The global impact on climate change switches to the use of renewable energy. Nowadays, the concentrated solar power (CSP) power plant received more attention in the researcher’s interest. The major problem associated with the CSP plant is the hot corrosion in the container materials exposed under phase change material (PCM). In the present study, Inconel 617 and 625 were used as container materials and Na2SO4 (50 Wt.%) +Diatomite (50 Wt.%) as PCM. The PCM based environmental assisted hot corrosion studies were conducted on container materials at 900°C for 40, 80, and 120 h duration. Differential scanning calorimetry (DSC) results confirmed the selected PCM melting temperature. The thermogravimetric analysis (TGA) is performed to determine the mass loss of the PCM. Fourier transform infrared (FT-IR) analysis confirmed the chemical compatibility between Na2SO4 and diatomite. After hot corrosion at 120 h for 900°C, the weight change values are 3.1 and 2.6 mg/cm2 for Inconel 617 and Inconel 625. In addition, the X-Ray Diffraction (XRD) and Scanning electron microscopy/energy dispersive spectroscopy (SEM/EDS) analysis were carried out to evaluate the hot corrosion behavior. The result indicates that the formation of NiO, Cr2O3, and SiO2 provides better resistance to corrosion in both container materials. Overall, Inconel 625 shows good corrosion resistance compared to Inconel 617 in a PCM environment.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Proceedings of the Institution of Mechanical Engineers, Part C: Journal of Mechanical Engineering Science
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.