Abstract
The effect of Sn on highpermeability grain-oriented silicon steel was studied by PHI-700 Auger electron spectroscopy (AES), JEM-2100 transmission electron microscopy (TEM) and electron back-scattered diffraction (EBSD) technology. The results show that (1) the magnetic properties could be significantly increased by adding Sn; (2) the primary grain size becomes smaller with the addition of 0.19 wt% Sn and the Goss orientation crystal nucleus become more numerous as well; (3) the grain boundary segregation of Sn is still obvious at 970 °C in hightemperature annealing process; and (4) the average size of precipitates becomes smaller with the addition of 0.19 wt% Sn; meanwhile the dispersion and the inhibitor are also promoted. These conclusions are in agreement with the experimental results.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.