Abstract
Ni55.5Mn21Ga23.5 and Ni54Mn22Ga23Sm1 films were prepared by radio frequency (RF) magnetron sputtering. The effect of Sm dopant on the morphologic and magnetic properties of Ni55.5Mn21Ga23.5 films was investigated. Sm doping can refine the particle size of the films from 100 to 60 nm, and further grain growth is not occurs even after annealing at 1073 K for 3.6 ks. Compared to Ni55.5Mn21Ga23.5 films, Sm-doped Ni54Mn22Ga23Sm1 films are easier to be magnetized and have a lower martensitic transformation temperature. In addition, the Curie temperature can also be adjusted, decreasing from 350 to 325 K after Sm doping. Martensitic transformation is not observed in the Sm-free films, which is close to the Curie temperature in the Sm-doped films, giving rise to the overlap of the structural and magnetic transition temperatures.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Minerals, Metallurgy, and Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.