Abstract
At the continuum length scale, mechanical properties of metals show relatively weak orientation dependence; however, they exhibit strong anisotropic behaviors as the size of sample decreases to micron and nanometer length scales. In this study, three-dimensional dislocation dynamics (DD) simulations are performed to investigate the orientation-dependent plasticity in submicron face-centered cubic (FCC) micropillars subjected to torsion. Accommodating results from atomistic modeling, updated surface nucleation schemes in DD models have been developed for three orientations ([001], [101], and [111]), allowing investigation of the dislocation microstructure evolution and the corresponding anisotropic mechanical response upon torsional loading and unloading. The DD simulation results show that the coaxial and hexagonal networks formed in [101] and [111] oriented nanopillars, respectively, exhibited excellent plastic recovery, while the rectangular network formed in the [001] crystal orientation was more stable and did not experience as much plastic recovery.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.