Abstract
Localized surface plasmon (LSP)-enhanced ultraviolet LEDs have been constructed via spin-coating Ag nanoparticles onto ZnO/SiO2 core/shell nanorod array/p-GaN heterostructures. Different from the previous reports where the dielectric spacer-layer thickness was determined only through photoluminescence (PL) characterization, the SiO2 shell thickness in this work is also optimized by actual electroluminescence (EL) measurements to maximize the enhancement. It is interesting to find that the enhancement ratios derived from PL and EL measurements demonstrate different thickness dependences on SiO2 shell: an optimal 3.5-fold PL enhancement was obtained at the SiO2 thickness of 16 nm, while an "abnormal" 7-fold EL enhancement was achieved at the thickness of 12 nm. Time-resolved spectroscopy studies, as well as theoretical estimations and numerical simulations, reveal that the higher-ratio EL enhancement stems from joint contributions, both internal-quantum-efficiency improvement induced by exciton-LSP coupling and light-extraction-efficiency improvement aroused by photon-LSP coupling.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.