Abstract
Studied here are the effects of sintering temperature of La0.6Sr0.4Co0.2Fe0.8O3-Ce0.9Gd0.1O2 (LSCF–CGO) cathodes on their microstructure and performance of intermediate-temperature solid oxide fuel cells (IT-SOFC). Phase composition, microstructure and electrochemical properties were investigated by X-ray powder diffraction (XRD), scanning electron microscopy and current-voltage characteristics measurement, respectively. The electrochemical performances of Ni–YSZ anode-supported SOFC having YSZ electrolyte (4 μm) with CGO interlayer (2 μm) are studied with LSCF–CGO (50:50 wt%) cathodes in the temperature range 600–800 °C using H2 as fuel and air as oxidant. The cathode microstructure was found to be less dense and to contain smaller grains as the sintering temperature was decreased in the range 1250–1150 °C. Results reveal that sintering temperature and electrode morphology have strong influence on electrochemical performances of the IT-SOFC. Highest maximum power density of ∼1.26 W/cm2 is achieved during cell testing at 800 °C with a cathode sintered at 1200 °C. However, cells with in-situ sintered LSCF–CGO cathode showed highest power density at 600 °C (0.48 W/cm2) because there is no particle coarsening at low sintering temperatures.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.