Abstract
The effects of sintering temperature on the surface morphology, roughness, and electrical properties of samarium-doped ceria (SDC)–carbonate (SDCC) composite electrolyte were examined. SDCC composite pellets were fabricated and sintered at various temperatures ranging from 500°C to 650°C. Brunauer–Emmett–Teller technique and atomic force microscopy were used to investigate the surface area and surface roughness of the composite materials, respectively. Conductivity measurements using impedance spectroscopy were conducted from 350°C to 550°C. The specific surface area of the pure SDC powder decreased from 8.85m2/g to 4.24m2/g after the carbonate phase was incorporated into the SDC phase with increasing particle size. The composite pellet sintering temperature affected the continuity between the two phases [SDC and (Li/Na) carbonate], roughness, mean particle size, and conductivity of the composite electrolyte. A fully dense SDCC composite electrolyte pellet sintered at 550°C exhibited a maximum ionic conductivity of 0.077S/cm at 550°C. In addition, 550°C was the minimum sintering temperature to achieve good wetting between the two phases, moderate particle size, low surface roughness, and high ionic conductivity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.