Abstract
In this research, Barium titanate (BT) additive in lanthanum modified lead zirconate titanate (PLZT) was used to stabilize the PLZT ceramics. Oxide powders were synthesized by mixed oxide synthetic route via a rapid vibro-milling technique. It was prepared with the chemical formula of 0.95 Pb0.91La0.09 (Zr0.65Ti0.35)0.9775O3 -0.05 BaTiO3 to investigate the dielectric properties of PLZT ceramics. The modified PLZT ceramics were fabricated at variation of sintering temperatures of 1200-1275°C for 4 hours. By employing X-ray diffraction (XRD), it was found a pure perovskite with rhombohedral structure. The relaxor behavior was observed from the dielectric measurements. The suitable sintering temperature of 0.95 PLZT - 0.05 BT was 1275°C (εr=10463, tanδ=0.0125 and Tm=70°C).
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.