Abstract

In this paper, the WC-16TiC-xTaC-9Co and Co are mixed together preparing for WC, (W, Ti, Ta) C. By high-energy ball milling, the powder is cold isostatic pressed and vacuum sintered by 1410°C, 1430°Cand 1450°C.The physical properties and the micrographs of samples are detected. The main conclusions are as following: sintered samples have the best comprehensive performance at 1450°C, the density of the sample is 99.7% and the actual density is 10.91g/cm3. The hardness is 92.8 HRA and the transverse rupture strength (TRS) is 1100MPa. The grain size grows up obviously with the high temperature. The average grain size of WC is 0.7μm and the average size of (W, Ti, Ta)C is 3μm.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.