Abstract
Silica ceramic cores prepared by heat-press molding were strengthened by impregnating silicone resin. The effect of heating treatment conditions on the properties of silica ceramic cores was analyzed. Results showed that the ambient bending strength increased from 9.3 ± 2.0 MPa to 24.8 ± 1.5 MPa by curing process at low temperature of 250 °C. However, further heating treatment at high temperature ranging from 1150 to 1300 °C made the strength of the samples lower than that of the cured samples owing to the decomposition of silicone resin. But the strength of the samples was still higher than that of raw samples. The increasing heating treatment temperature promoted an increase in the strength by a densification process.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.