Siliconboron carbonitride ceramics (SiBCN) were introduced into porous Si3N4 substrates via low pressure chemical vapor deposition and infiltration from SiCl3CH3-NH3-BCl3-H2-Ar system. To improve the electromagnetic wave(EMW) absorbing properties, the molar ratio, nCH3SiCl3/(nNH3+nBCl3), was increased based on thermodynamics analysis. The results show that nanosized silicon carbide crystals and free carbon dispersed uniformly in the amorphous SiBCN phase, resulting in suitable dielectric properties and improved absorption capabilities of SiBCN-Si3N4 ceramics. Additionally, with increasing SiBCN ceramics loading, the amount of nanocrystals and interface between nanocrystals and amorphous SiBCN phase increased, leading to enhanced polarization and dielectric loss of the composite ceramics. When SiBCN content was up to 3.64wt%, the electromagnetic reflection coefficient (RC) of SiBCN-Si3N4 composite ceramics reached −40dB (>99.97% absorbing) with the effective electromagnetic absorbing bandwidth of 3.64GHz in the X-band. This study makes it possible to fabricate SiBCN-based composite materials with excellent EMW absorbing properties at a low temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.