Abstract
Al-Si-Fe plates with Si contents of 4.5, 9 and 11 mass %, unmodified and Sr-modified, were quasi-directionally solidified in sand moulds with chills at one end. The size and nature of the Fe-rich intermetallics were determined along the plates. Two forms of the intermetallic were observed, α-Al8FeSi and β-Al5FeSi, in proportions and scale dependent on the cooling rate and the Si concentration. The size of the β-phase increased with the concentration of Si at low cooling rates. At high cooling rates the tendency to form α-Al8FeSi phase increased with increasing Si content reducing the size of the β-plates. Modification generally increased the size of the pre-eutectically formed plates while reducing the post eutectically formed ones.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.