Abstract
The effects of Si addition and of deposition temperature on the precipitation processes of Al2Cu (θ) and Si particles in Al-Cu-Si alloy films were studied with in-situ hot stage transmission electron microscopy (TEM). Deposition of an Al-1.5Cu-1.5Si (wt%) film at 305∘C, in the three-phase, Al(α)-Al2Cu-Si region resulted in formation of fine, uniformly distributed spherical θ -phase particles due to the coprecipitation of the θ and Si phase particles during deposition. For deposition in the two-phase, Al(α)-Si region (435∘C), fine θ -phase particles precipitated during wafer cooldown, while coarse Si nodules formed at the sublayer interface during deposition. In-situ heat treatment of the film revealed that excess Si existed in a supersaturated Al matrix. Si addition decreased film susceptibility to corrosion induced by the θ -phase precipitates, since extensive Cu segregation can be reduced by coprecipitation at 305∘C and the Al matrix supersaturated with Si reduced galvanic action with respect to the θ -phase precipitate.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.