Abstract
Abstract Polycrystalline aluminium Al99.5 was deformed through the combination of equal-channel angular pressing (ECAP) by B route (4, 8 and 16 passes) and then by the hydrostatic extrusion (HE) using the cumulative way of deformation, just to the achieving the final wire diameter d = 3 mm. The microstructure of samples was investigated by means light microscopy (LM). Additionally the microhardness measurement and the tensile test were performed to determine the level of aluminium hardening. The texture was determined by using the Brucker Advance D8 equipment. The aim of the research was to determine the influence of severe plastic deformation exerted in the process of equal-channel angular pressing (ECAP) and hydrostatic extrusion (HE) on the microstructure and properties of polycrystalline aluminium Al99.5. The microstructure observations both after the HE process and the combination of ECAP + HE revealed the elongated to the extrusion direction grains and numerous bands and shear bands. The bands and shear bands most clearly revealed at the perpendicular section. The performed investigations showed that with the increase of the deformation the aluminium level hardening increase. The highest properties of tensile strength - UTS = 218 MPa and microhardness level HV0.1 = 46 were obtained after 8 ECAP + HE.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.