Abstract
The influence of 1.0–5.0-nm-thick Ti and Fe seed layers on self-organized Ag nanostructures grown on MgO(001) substrates after annealing was investigated and compared. Atomic force microscopy results indicated that the insertion of Ti and Fe seed layers between the substrate and Ag promoted thermal agglomeration, thereby resulting in the formation of a nanodot array. Moreover, the size and spacing of the Ag/Ti and Ag/Fe nanodots changed significantly and irregularly, respectively, with increasing thickness of the seed layers. X-ray diffraction measurements revealed that the insertion of the Ti seed layer promoted epitaxial growth of Ag nanodots; Ag/Fe nanodots, in contrast, grew non-epitaxially. Based on the results, it can be concluded that the differences between the effects of the Ti and Fe seed layers are mainly due to the thermal equilibrium state between the seed layer elements and Ag.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.