Abstract
The effects of Sc and Zr on the shape, size, and number density of Al6(Mn,Fe) phase in Al–5Mg–0.7Mn alloys were investigated by this article. The results showed that Sc and Zr can form strengthening particles of Al3Sc and Al3(Sc,Zr), which have the effect of refining grains and modifying the morphology and distribution of Al6(Mn,Fe) phase. The OM, SEM, and TEM images indicate that with the formation of primary Al3Sc and Al3(Sc,Zr), the shape of Al6(Mn,Fe) became more regular, size of Al6(Mn,Fe) became smaller, and the number density of Al6(Mn,Fe) increased when compared with base alloy. Zr could motivate the precipitation of primary Al3(Sc,Zr) and Al–5Mg–0.7Mn–0.2Sc–0.2Zr had better refining effect than Al–5Mg–0.7Mn–0.4Sc. The grain refinement and finely dispersed Al6(Mn,Fe) phase can improve the mechanical properties such as yield strength and ultimate tensile strength and the corrosion resistance by the results of intergranular corrosion (IGC) also improved.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.