Abstract
Alkali-activated slag-fly ash-silica fume cement (AA-SFSC) is suitable for the production of clinkerless alkali-activated binder-based ultra-high strength concrete (AAB-UHSC). However, using a relatively low water-to-binder ratio and a high alkali dosage to prepare AAB-UHSC leads to rapid setting and a loss of flowability. Thus, the setting time of the AA-SFSC needs to be controlled. In our study, the effect of various retarders (single retarder borax and hybrid retarder a combination of zinc nitrate hexahydrate and sodium gluconate) on the AA-SFSC was investigated. The setting characteristics, reaction kinetics, mechanical performance, pore structure alteration, mineralogical and molecular transformations, and microstructure of the AA-SFSC were systematically examined. The results showed that both borax and a combination of zinc nitrate hexahydrate and sodium gluconate had a remarkable retarding effect on AA-SFSC with a low water-to-binder ratio and high alkali dosage. However, borax had a detrimental effect on the compressive strength, and the effect of adding zinc nitrate hexahydrate and sodium gluconate as the hybrid retarders on the compressive strength depended on the dosage; and a dosage of 1% zinc nitrate hexahydrate and 2% sodium gluconate was recommended for prolonging the setting time of AA-SFSC without compromising the mechanical performance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.