Effect of relative humidity cycles accompanied by intermittent start/stop switches on performance degradation of membrane electrode assembly components in proton exchange membrane fuel cells

Abstract

The performance degradation of membrane electrode assembly (MEA) components in proton exchange membrane fuel cell (PEMFC) is studied by designing relative humidity (RH) cycles accompanied by intermittent start/stop switches. Cathode catalyst activity, permeability and resistance of proton exchange membrane (PEM) as well as cell performance are monitored during the test procedure. The interfaces of MEA, the catalyst particle distribution near the cathode inlet are characterized by SEM and TEM, respectively. The results demonstrate both the overall H2 permeability and crossover current of PEM are doubled compared with its initial properties. Signs of PEM degradation, including periodical thinning, cracks and pinholes formation, are observed after 300 RH cycles and 40 times of start/stop switches. The average Pt particle size increases by more than 75%, and the cathode electrochemical surface area decreases by 48% after the test procedure. Meanwhile, the cathode catalyst layer becomes looser due to the dissolution of some smaller Pt particles and catalyst agglomeration in the RH cycles and the high potential during the intermittent start/stop switches. The membrane resistance demonstrates downshift variation during the RH cycles. PEMFC performance, however, decays due to the chemical and electrochemical attack as well as the mechanical stresses.