Abstract
The barium ferrite BaFe12O19 with c-plane anisotropy, which possessed relative high saturation magnetization and low coercivity, had been synthesized by hydrothermal method with different reaction time of 5 h, 8 h,11 h,14 h, and 17 h. The X-ray diffraction (XRD), field emission scanning electron microscope (FESEM) and vibrating sample magnetometer (VSM) were used to study the phase composition, microstructure and magnetic properties of barium ferrite, respectively. The results showed the intensities of the peak were enhanced and there was no impurity phase. With the prolonging of the reaction time to 11 h, 14 h and 17 h, the grain size increased, and the equivalent diameter was about 1 μm, and the thickness was about 100 nm. When the reaction time was 17 h，the coercivity of barium ferrite was 1104 Oe. The reduction of coercivity was ascribed to the increase of particle size and the reduction in magnetic anisotropy.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.