Abstract
The effect of rare earth (RE) on creep rupture of economical 21Cr-11Ni-N heat-resistant austenitic steel was investigated at 650 °C under different stress levels. It was found that RE could increase the time to creep rupture, especially at long-term creep duration. The logarithm of the time to creep rupture (lgtr) was a linear function of the applied stress (σ). RE addition was favorable to generating a high fraction of low-coincidence site lattice (CSL) boundaries which was a possible cause for improving the creep rupture resistance. The fracture surface of RE-added steel exhibited less intergranular cracks suggesting the alteration on the nature of grain boundaries due to the presence of RE. RE addition changed the morphology of the intergranular chromium carbides from continuous network shape to fragmentary distribution which was another cause for longer creep duration. These results strongly suggested that the effect of RE alloying played a crucial role in improving the creep rupture resistance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.