Abstract
AbstractBACKGROUND: Poly(butylene adipate‐co‐terephthalate) (PBAT) has attracted wide interest as a biodegradable polymer. However, its use is restricted in certain applications due to its low melting point.RESULTS: PBAT was treated using γ‐radiation. The radiation features were analyzed using Soxhlet extraction, and the ratio of chain scission and crosslinking and gelation dose were determined using the classical Charlesby–Pinner equation. The results showed that PBAT is a radiation‐crosslinkable polymer. The degree of crosslinking increased with increasing radiation dose; the relation between sol fraction and dose followed the Charlesby–Pinner equation. Differential scanning calorimetry analyses showed that the melting temperature (Tm) and the heat of fusion (ΔHm) of PBAT exhibited almost no change in the first scan. The second scan, however, showed a decrease in Tm and ΔHm. The glass transition temperature of irradiated PBAT increased with increasing radiation dose. The weight loss of control and irradiated PBAT resulting from thermal degradation was a one‐step process. Moreover, the tensile strength and elongation at break decreased with an increase in radiation dose. However, the Young's modulus and stress at yield were not greatly affected by γ‐radiation.CONCLUSION: PBAT can be crosslinked using γ‐radiation. The crosslinking efficiency is relatively low. The thermal and mechanical properties of PBAT are affected by γ‐radiation. Copyright © 2009 Society of Chemical Industry
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.