Effect of Q235 Hot-Dip Galvanized and Post-Casting T6 Heat Treatment on Microstructure and Mechanical Properties of Interfacial between AZ63 and Q235 by Solid-Liquid Compound Casting

Abstract

AZ63 sacrificial anode is widely used to protect buried metal pipelines and reinforced concrete structures and so on. The interfacial metallurgical bonding between AZ63 sacrificial anode and Q235 wiring terminal directly affects its cathodic protection performance. Therefore, microstructure and mechanical properties of interfacial between AZ63 and Q235 by solid–liquid compound casting with hot-dip galvanized and post-casting solution-aging treatment (T6) were investigated. The results indicate that hot-dip galvanizing on the surface of Q235 is beneficial to the formation of intermetallic compounds at the interface. At the same time, it can promote the metallurgical bonding of the interface between AZ63 and Q235. After T6 heat treatment, the intermetallic compound at the interface between AZ63 and galvanized Q235 was refined. The electron-probe microanalyzer (EPMA) revealed that the intermetallic compounds at the interfaces between AZ63 and galvanized Q235 were Fe2Al5 before and after T6 treatment. Push-out testing and microhardness were used to investigate the mechanical properties of interface between AZ63 and Q235. It is shown that the hot-dip galvanization of the Q235 surface and T6 treatment were beneficial to improve the metallurgical bonding shear strength and microhardness of the interface. After T6 heat treatment, the highest shear strength at the interface between AZ63 and galvanized Q235 was up to 31.9 ± 1.9 MPa.