Abstract To improve the mechanical properties of carbon-bonded carbon fiber (CBCF) composites, they are firstly fabricated by chemical vapor deposited (CVD) pyrolytic carbon (PyC) coating layer on the carbon fiber surface, and then modified by zirconium boride (ZrB 2 ) using three cycles of precursor infiltration and pyrolysis (PIP) process. The effects of different PyC interface thickness on the microstructure and mechanical properties of ZrB 2 modified PyC coated CBCF (PyC–CBCF/ZrB 2 ) composites were studied and characterized. As the PyC thickness increased from 0.5 to 3.6 μm, the flexural properties of PyC–CBCF/ZrB 2 composites are noticeably enhanced in x / y and z direction, respectively. Mechanical enhancements for PyC–CBCF/ZrB 2 composites are mainly attributed to the effective interface bonding between carbon fiber and PyC, crack deflection and branching within the laminar PyC layer and carbon fiber pullout from PyC interface coating.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.