Abstract
AbstractThe effect of a pulsed laser irradiation (Nd:YVO4, 1064 nm) in air on the surface morphology and chemical composition of silicon carbide and on the adhesion with an epoxy adhesive was investigated. Scanning and transmission electron microscopies, atomic force microscopy, and X‐ray photoelectron spectroscopy revealed that the laser treatment reduced the contamination level of the surface and induced the formation of a silica‐based nanostructured columnar layer on the SiC surface. The mechanism for the formation of five different microstructural regions is described in this paper. In addition, the formation of a 5‐10‐nm‐thick graphite layer between the oxide layer and SiC was observed. The joining test with Hysol® EA9321 showed that the nanostructured columnar silica layer was completely infiltrated by the adhesive, thus leading to a significant increase in the joined specific area and a mechanical interlocking at the adhesive/substrate interface. Nevertheless, the apparent shear strength of the joined SiC samples slightly decreased after the laser processing of the surfaces from about 42 MPa for lapped SiC to about 35 MPa for laser‐nanostructured SiC. The formation of the graphite layer was found to be responsible of the poor adhesion properties of the SiC surfaces modified by the laser radiation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Applied Ceramic Technology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.