Effect of pulse current on the creep ageing behavior of pre-strained 2195 Al-Li alloy

Abstract

Pre-strained aluminum lithium (Al-Li) alloy plates have ultra-high strength and comprehensive performance after aging treatments, and are widely used in the aerospace industry. The initial increase in dislocation density caused by these pre-strains will significantly affect the evolution of deformation, microstructure, and mechanical properties during the pulse current assisted creep ageing forming process. Therefore, the effect of pulse current on the creep ageing behavior of 2195 Al-Li alloy with different pre-strains (0%, 4%, and 8%) was investigated. As the pulse current increases within the first 1h creep aging process of the various pre-strain samples, the 1h creep strain significantly increases and the subsequent steady-state creep rate slightly reduce. Moreover, the larger the pre-strain, the higher the total creep strain. Pulse current promotes the movement and recovery of initial dislocations, and promotes the fine formation of T1 phase and suppresses the nucleation of θ' and phase, thereby improving mechanical properties. Compared with the conventional creep ageing process, the pulse current acting on pre-strained 2195 Al-Li alloy significantly increased the peak aged strengthen and shorten the peak aging time. Meanwhile, the peak time platform period has also been significantly extended. It is evident that the application of pulse current assisted creep ageing forming process to pre-strained 2195 Al-Li alloy plates can significantly improve formability and mechanical properties, enlarges the forming process window and realize collaborative manufacturing of Al-Li alloy component shape and performance.