Abstract
It is difficult to effectively improve the low bonding strength of TA1/304 clad plates. This study proposes a new process for applying pulse current (1500 A, 500 Hz, 50% duty cycle) to TA1/304 clad plates during the rolling process, which changes the interface microstructure and effectively improves the bonding strength of the clad plates. The influence of the pulsed current on the interface microstructure and bonding strength was systematically studied. The results indicate that the clad plate is initially bonded at 750 °C and 35% reduction ratio under electrically-assisted rolling (EAR), and finally the higher bonding strength is obtained at 850 °C and 48% reduction ratio, reaching 395 MPa. The strengthening of the interface element diffusion and grain refinement under the action of the pulsed current are important reasons for the improvement in the bonding strength of the clad plate. This discovery provides new ideas for the preparation of clad plates with high bonding performance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.