Abstract
AbstractCarbon nanotube‐reinforced polymer composites are being investigated as promising new materials having enhanced physical and mechanical properties. With regards to mechanical behavior, the enhancements reported thus far by researchers are lower than the theoretical predictions. One of the key requirements to attaining enhanced behavior is a uniform dispersion of the nanotubes within the polymer matrix. Although solvent mixing has been used extensively, there are concerns that any remaining solvent within the composite may degrade its mechanical properties. In this work, a comparison is carried out between solvent and “solvent‐free” dry mixing for dispersing multiwall carbon nanotubes in polypropylene before further melt mixing by extrusion. Various weight fractions of carbon nanotubes (CNTs) are added to the polymer and their effect on the mechanical properties of the resulting composites is investigated. Enhancements in yield strength, hardness, and Young's modulus when compared with the neat polymer, processed under similar conditions, are observed. Differences in mechanical properties and strain as a function of the processing technique (solvent or dry) are also clearly noted. In addition, different trends of enhancement of mechanical properties for the solvent and dry‐mixed extrudates are observed. Dry mixing produces composites with the highest yield strength, hardness, and modulus at 0.5 wt% CNT, whereas solvent mixing produces the highest mechanical properties at CNT contents of 1 wt%. It is believed that this difference is primarily dependent on the dispersion of CNTs within the polymer matrix which is influenced by the processing technique. Field emission scanning electron microscopy analysis shows the presence of clusters in large wt% CNT samples produced by dry mixing. Samples produced by solvent mixing are found to contain homogeneously distributed CNTs at all CNT wt fractions. CNT pull‐out is observed and may explain the limited enhancement in mechanical properties. POLYM. COMPOS., 2010. © 2009 Society of Plastics Engineers
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.