Abstract
The fatigue reliability of a diecast AlSi11Cu2(Fe) alloy radiator has been investigated at different pressure amplitudes and thermal exposure. Based on failure mode analysis, two failure mechanisms are observed during fatigue testing, i.e. leakage at the interface between the diecast element and the plug, and fatigue fracture of a radiator element. Fatigue life tests have been carried out at two different pressure amplitudes, 3 and 4 MPa, and two holding temperatures, 40 and 60 °C, respectively. The results reveal how the main cause of failure is related to the fatigue failure of a radiator element in the whole heating system. This is due to casting defects such as gas porosity and oxides which are formed during the filling phase of the die cavity in high-pressure die casting. Furthermore, casting defects increase the leakage failure and reduce the fatigue life of the radiator. An increase of the holding temperature increases the frequency of leakage failure of radiators.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.