Abstract
Antimony trioxide was prepared, using antimony potassium tartarate as starting material, via forward and reverse precipitation technique. The characteristics of the resulting antimony oxides were determined by BET surface area method, differential thermogravimetry analysis (DTG), X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FT-IR) and SEM. The DTG curves for all uncalcined samples showed only a single endothermic peak which indicated that the sample is antimony trioxide. Unlike forward precipitation technique which resulted in a single antimony trioxide phase which is senarmontite, reverse precipitation technique produced antimony trioxide with both senarmontite and valentinite phase. Upon calcinations at 723 K, a small amount of Sb 2O 4 with cervantite phase was formed at the expense of Sb 2O 3 senarmontite phase as detected from the XRD pattern and infrared spectrum of RSb. The effect of preparation route on the properties of the antimony trioxide produced was clearly demonstrated.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.