Abstract
The liquid phase separation process and solidification process of ternary Al81.3Sn12.3Cu6.4 monotectic alloy was accomplished with a 20kHz ultrasonic field in the power range up to 500W. As ultrasound power rised, the coarse primary (Al) dendrites turned into fine equiaxed grains, whose size decreased by one order of magnitude as that during static solidification. Meanwhile, rather than pronounced segregation of large secondary (Sn) blocks in the alloy sample solidified under static condition, tiny secondary (Sn) droplets dispersed homogenously within the (Al) matrix in the presence of ultrasound. Under the highest ultrasound power of 500W, the spherical ternary (Al+Sn+θ(Al2Cu)) monotectic cells formed. The refinement of primary (Al) dendrites and uniform distribution of secondary (Sn) droplets induced by power ultrasound result in the improvement of microhardness, wear resistance, compressive and yield strength of ternary Al81.3Sn12.3Cu6.4 monotectic alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Progress in Natural Science: Materials International
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.